孙永欣; 赵青; 刘力; 常爱民; 文彬; 杨忠波; 陈志慧
Source Publication硅酸盐学报

以Zr(OH)4和Y(OH)3的共沉淀为前驱体,在碱性介质中用微波水热法合成摩尔分数为8%的氧化钇稳定氧化锆(yttria stabilized cubic zirconia,YSZ)纳米粉体。通过X射线粉末衍射仪、透射电镜和等离子发射光谱等表征粉体的性能。研究了微波水热法的反应温度、时间和前驱物浓度 对反应产物形貌、粒度等的影响。获得了制备具有纳米立方相结构的YSZ粉体的最佳工艺参数:粉体粒度为5~10nm,产物纯度为99%。结果表明:温度为 200℃时,产物粒径较小且均匀。微波水热制备YSZ的最佳反应时间为20~40min。前驱物中Zr^4+的最佳浓度为0.2mol/l。增大碱性介质 KOH的浓度对产物的晶型和粒度影响不大。;Cubic phase ZrO2-8% (in mole)Y2O3, nano-powders were prepared in basic media by the microwave-hydrothermal method, with Zr(OH)4 and Y(OH)3 co-precipitated from ZrO(NO3)2·2H2O and Y(NO3)3·6H2O solutions as the precursors. The resultant precipitates were characterized by X-ray diffraction, transmission electron microscopy and inductively coupled plasma-optima emission spectrometry. Influents of solution content, temperature and time on the crystalline type and morphology of yttrium stabilized cubic zirconia were studied. Well dispersed and narrowly distributed ZrO2 -8%Y2O3, nanopowders with particle sizes of 5-10 nm were obtained under the given process conditions. The best conditions for the microwave-hydrothermal method are as follows: reaction time of 20-40 min, precursor content of 0.2 mol/l, temperature of 194-200℃ , and KOH content of 0.4 mol/l . The product purity is 99% in mass.

Keyword氧化钇稳定氧化锆 纳米 微波水热法
Subject AreaEngineering (Provided By Thomson Reuters)
Indexed ByCSCD
Citation statistics
Document Type期刊论文
Affiliation中国科学院新疆理化技术研究所;中国科学院研究生院; 兰州化学物理研究所
Recommended Citation
GB/T 7714
孙永欣,赵青,刘力,等. 微波水热合成ZrO2-8%Y2O3纳米粉体[J]. 硅酸盐学报,2005,33(10):1255-1258.
APA 孙永欣.,赵青.,刘力.,常爱民.,文彬.,...&陈志慧.(2005).微波水热合成ZrO2-8%Y2O3纳米粉体.硅酸盐学报,33(10),1255-1258.
MLA 孙永欣,et al."微波水热合成ZrO2-8%Y2O3纳米粉体".硅酸盐学报 33.10(2005):1255-1258.
Files in This Item:
File Name/Size DocType Version Access License
微波水热合成ZrO_2_8_Y_2O_3(515KB)期刊论文作者接受稿开放获取CC BY-NC-SAView Application Full Text
Related Services
Recommend this item
Usage statistics
Export to Endnote
Google Scholar
Similar articles in Google Scholar
[孙永欣]'s Articles
[赵青]'s Articles
[刘力]'s Articles
Baidu academic
Similar articles in Baidu academic
[孙永欣]'s Articles
[赵青]'s Articles
[刘力]'s Articles
Bing Scholar
Similar articles in Bing Scholar
[孙永欣]'s Articles
[赵青]'s Articles
[刘力]'s Articles
Terms of Use
No data!
Social Bookmark/Share
File name: 微波水热合成ZrO_2_8_Y_2O_3纳米粉体.pdf
Format: Adobe PDF
This file does not support browsing at this time
All comments (0)
No comment.

Items in the repository are protected by copyright, with all rights reserved, unless otherwise indicated.