In this work, Pb0.97La0.02(Zr0.98Ti0.02)O-3 (PLZT 2/98/2) antiferroelectric (APE) thick films were successfully deposited on LaNiO3/Si(100) substrates by polyvinylpyrrolidone (PVP)-modified chemical solution. Each wet layer was first dried at 300 degrees C and then pyrolyzed at higher temperature B of 600, 650, or 700 degrees C, respectively. The effects of the pyrolyzed temperature B on the microstructure and the energy-storage performance of the AFE films were investigated in detail. As the increasing of the pyrolyzed temperature, the crystallized PLZT 2/98/2 films displayed a more uniform and dense surface microstructure. As a result, the dielectric properties, AFE characterization, and energy-storage performance were remarkably improved for the APE thick films pyrolyzed at higher temperature. The maximum energy-storage density of 58.1 J/cm(3) and the corresponding energy-storage efficiency of 37.3% were obtained in the PLZT 2/98/2 films pyrolyzed at 700 degrees C for every layer.
Inner Mongolia Univ Sci & Technol, Sch Met & Mat, Baotou 014010, Peoples R China;Chinese Acad Sci, Xinjiang Tech Inst Phys & Chem, Xinjiang Key Lab Elect Informat Mat & Devices, Urumqi 830011, Peoples R China;Xi An Jiao Tong Univ, Sch Phys, Xian 710049, Peoples R China
Wang Ying,Hao Xihong,Yang Jichun,et al. Fabrication and energy-storage performance of (Pb,La)(Zr,Ti)O-3 antiferroelectric thick films derived from polyvinylpyrrolidone-modified chemical solution[J]. JOURNAL OF APPLIED PHYSICS,2012,112(3):-.