题名: 耐水性膨胀蛭石板材的研制
其他题名: development of water-resistance expanded vermiculite board
作者: 刘文; 陈朝阳; 闫世友
关键词: vermiculite ; soluble glass ; silicone-acrylic resin ; water absorption
刊名: 应用化工
发表日期: 2011
卷: 40, 期:6, 页:993-996
资助者: 新疆自治区高技术发展计划基金项目(200816121);乌鲁木齐市科技攻关基金项目(Y08211004)
摘要: 以膨胀蛭石、水玻璃、K2S iF6、硅丙树脂为原料,利用热压成型工艺,制备了具有耐水性好、强度高、导热系数低等优异性能的蛭石保温防火制品。研究了各组分配比以及成型时的压缩率对蛭石保温防火制品的抗压强度、吸水率、导热系数等物理性能的影响。结果表明,m(K2S iF6)/m(水玻璃)=0.022,m(水玻璃)/m(膨胀蛭石)=1.3,压缩率为74%,硅丙树脂掺量为14%,150℃、0.2 MPa时热压3 h可制备出抗压强度为4.58 MPa,导热系数为0.084 W/m.k,吸水率为5%的蛭石保温防火制品,具有可锯、可钉、可刨等机械加工性能。
英文摘要: The vermiculite-based fire resistant and thermally insulating product was made of expanded vermiculite,soluble glass,K2SiF6,silicone-acrylic resin by hot pressing method,which is provided with excellent waterproof,high strength,low thermal conductivity,etc.The effect of ingredient proportion and compression ratio on compressive strength,water absorption and thermal conductivity were studied systematically.Under the optimum conditions:m (K_2SiF_6)/m (soluble glass)= 0.022,m (soluble glass)/ m(expanded vermiculite)= 1.3,compression ratio 74% ,14% silicone-acrylic resin,the fire resistant and thermally insulating board with compressive strength 4.58 MPa,thermal conductivity 0.084 W/m k,water absorption 5% can be produced by hot pressing method at 150 ℃ for 3 h under the pressure of 0.2 MPa,and good machinability is obtained simultaneously.
内容类型: 期刊论文
URI标识: http://ir.xjipc.cas.cn/handle/365002/1566
Appears in Collections:材料物理与化学研究室_期刊论文

Files in This Item:
File Name/ File Size Content Type Version Access License
耐水性膨胀蛭石板材的研制.pdf(376KB)期刊论文作者接受稿开放获取View 联系获取全文

作者单位: 中国科学院新疆理化技术研究所;中国科学院研究生院

Recommended Citation:
刘文,陈朝阳,闫世友. 耐水性膨胀蛭石板材的研制[J]. 应用化工,2011,40(6):993-996.
Service
Recommend this item
Sava as my favorate item
Show this item's statistics
Export Endnote File
Google Scholar
Similar articles in Google Scholar
[刘文]'s Articles
[陈朝阳]'s Articles
[闫世友]'s Articles
CSDL cross search
Similar articles in CSDL Cross Search
[刘文]‘s Articles
[陈朝阳]‘s Articles
[闫世友]‘s Articles
Related Copyright Policies
Null
Social Bookmarking
Add to CiteULike Add to Connotea Add to Del.icio.us Add to Digg Add to Reddit
文件名: 耐水性膨胀蛭石板材的研制.pdf
格式: Adobe PDF
所有评论 (0)
暂无评论
 
评注功能仅针对注册用户开放,请您登录
您对该条目有什么异议,请填写以下表单,管理员会尽快联系您。
内 容:
Email:  *
单位:
验证码:   刷新
您在IR的使用过程中有什么好的想法或者建议可以反馈给我们。
标 题:
 *
内 容:
Email:  *
验证码:   刷新

Items in IR are protected by copyright, with all rights reserved, unless otherwise indicated.

 

 

Valid XHTML 1.0!
Powered by CSpace