Alternative Titlestudy on growth and properties of k2cab8o26h24 crystal
罗将; 潘世烈; 韩健
Source Publication人工晶体学报

采用室温溶液法生长K2CaB8O26H24晶体,并得到尺寸为11mm×6 mm×5 mm的单晶.该晶体属于正交晶系,P212121空间群,晶胞参数为a=1.15520(2)nm,b=1.24751(3)nm,c=1.65768(4)nm.红外光谱测量证实晶体结构中含有BO33-和BO54-基团.透过光谱表明K2CaB8O26H24晶体紫外吸收边在200nm左右.K2CaBsO26H24晶体粉末倍频效应(SHG)测试表明该化合物具有倍频效应,信号强度约为KH2PO4晶体的0.3倍.

Other Abstract

A single crystal K2CaB8O26H24 with sizes of 11 mm × 6 mm × 5 mm was grown by room temperature solution method. It belongs to the orthorhombic system, space P212121, and lattice parameters a=1.15520(2) nm, b=1.24751(3) nm, c=1.65768(4) nm. The measurement of the infrared spectrum indicates that the basic anionic group is the BO33- and BO45-. The transmittance spectrum shows that the UV cut-off wavelength of K2CaB8O26H24 is about 200 nm. Its powder second harmonic effect is about 0.3 times of KDP crystal.

Keyword室温溶液法 K2cab8o26h24 倍频
Subject AreaCrystallography (Provided By Thomson Reuters)
Indexed ByCSCD
Citation statistics
Document Type期刊论文
Recommended Citation
GB/T 7714
罗将,潘世烈,韩健. K2CaB8O26H24晶体的生长及其性质的研究[J]. 人工晶体学报,2011,40(3):548-551.
APA 罗将,潘世烈,&韩健.(2011).K2CaB8O26H24晶体的生长及其性质的研究.人工晶体学报,40(3),548-551.
MLA 罗将,et al."K2CaB8O26H24晶体的生长及其性质的研究".人工晶体学报 40.3(2011):548-551.
Files in This Item:
File Name/Size DocType Version Access License
K2CaB8O26H24晶体的生长及其性(385KB)期刊论文作者接受稿开放获取CC BY-NC-SAView Application Full Text
Related Services
Recommend this item
Usage statistics
Export to Endnote
Google Scholar
Similar articles in Google Scholar
[罗将]'s Articles
[潘世烈]'s Articles
[韩健]'s Articles
Baidu academic
Similar articles in Baidu academic
[罗将]'s Articles
[潘世烈]'s Articles
[韩健]'s Articles
Bing Scholar
Similar articles in Bing Scholar
[罗将]'s Articles
[潘世烈]'s Articles
[韩健]'s Articles
Terms of Use
No data!
Social Bookmark/Share
File name: K2CaB8O26H24晶体的生长及其性质的研究.pdf
Format: Adobe PDF
All comments (0)
No comment.

Items in the repository are protected by copyright, with all rights reserved, unless otherwise indicated.