Based on spinel-type semiconducting electroceramics, negativetemperaturecoefficient (NTC) thermistor materials, Ni0.9Co0.8Mn1.3-xFexO4 (0 <= x <= 0.7), with different compositions were synthesized by a co-precipitation method. The optimal pH value and the influence ofFe3+ doping during the synthesis processing were discussed. As-prepared Ni0.9Co0.8Mn1.3-xFexO4materials were characterized by DT/TGA, XRD, FTIR, SEM, electrical measurement and impendance analysis. It was found that, as the Fe doping content in the Ni0.9Co0.8Mn1.3-xFexO4 samples increased, both the grain size and the density decreased. The as-sintered Ni0.9Co0.8Mn1.3-xFexO4 samples presented a single-phase cubic spinel structure. The impendance diagram indicated that the grain boundary resistance was dominant in the overall impendance ofNi0.9Co0.8Mn1.3-xFexO4 NTC ceramicmaterials. The value of rho(25). B-25/50, slope and activation energy for the samples Ni0.9Co0.8Mn1.3-xFexO4 sintered at 1200 degrees C were in the range of 453.1-2411 Omega cm, 3103-3355 K, 3.27325-3.43149 and 0.28207-0.29325 eV, respectively. This suggests that the electrical properties can be adjusted to desired values by controlling the Fe3+ ion doping content.